I like the vinegar idea, I was noticing that the hamon was not very visable. I applied some flitz wax as an anticorrosive.
I like the vinegar idea, I was noticing that the hamon was not very visable. I applied some flitz wax as an anticorrosive.
Yep, the patina from the etching goes away with usage and fades with age - well, the difference fades. So, a spa treatment could be good for the looks.
Hamon: technically, it's not hamon. Hamon is the visual effect when mono-steel is differentially hardened - so when you dip it in some kind of acid it etches differently.
What you have is a sanmai construction - the principle is the same - harder steel resist the etch more so there's a difference in colour - but it's actually two different steels.
This is hamon:
![IMG_20180110_160732.jpg](https://steemitimages.com/DQmdXwrke2JMEuYuCwUVMz7Dj6jTRor5rPwBawgUBdhoNvS/IMG_20180110_160732.jpg)
Edit: wax - that's OK -anything that keeps the blade from direct exposure to the environment.
nice